PP Staple Fiber can be used in non-wovens,automotive interiors, geo-textiles, speaker cloth and needle carpet etc.
Products line
Cotton fiber(used in spinning) ,wool fiber(used in non-woven) ,color fiber,
Anti-flaming fiber,far-IR,hydrophily
Specification
1.linear density:1.7-22.2dtex
2.Length:38mm,51mm,65mm,76mm,102mm,130mm
Certificate
ISO CE ASTM
Property
1.It has good wicking and flexibility and excellent net form and carding and thermal bonding.
2.High strength and crimp elasticity,light weight,low melting-point,good permeability,anti-acid and alkaline,excellent abrasion resistance.
Application
Needle punched carpet,automativetrim,non-
woven geotextile,high strength ecological fabric,rope,decorating materials,medtech,filter products.
Technical specification
NO. | ITEM | UNIT | 1.7~3.3 DTEX | 3.4~7.8 DTEX | ||||||||
TOP | GRADE.1 | GRADE.2 | GRADE.3 | TOP | GRADE.1 | GRADE.2 | GRADE.3 | |||||
1 | Break Strength | Cn/dtex | ≥4.0 | ≥3.5 | ≥3.2 | ≥2.9 | ≥3.5 | ≥3.0 | ≥2.7 | ≥2.4 | ||
2 | Elongation | % | ≤60.0 | ≤70.0 | ≤80.0 | ≤90.0 | ≤70.0 | ≤80.0 | ≤90.0 | ≤100.0 | ||
3 | Linear density deviation | % | ±3.0 | ±8.0 | ±8.0 | ±10.0 | ±4.0 | ±8.0 | ±10.0 | ±12.0 | ||
4 | Length deviation | % | ±3.0 | ±5.0 | ±7.0 | ±9.0 | - | - | - | - | ||
5 | Defect | mg/100g | ≤5.0 | ≤20.0 | ≤40.0 | ≤60.0 | ≤5.0 | ≤25.0 | ≤50.0 | ≤70.0 | ||
6 | over-length fibre | mg/100g | ≤5.0 | ≤20.0 | ≤40.0 | ≤60.0 | ≤5.0 | ≤20.0 | ≤40.0 | ≤60.0 | ||
7 | over-length fibre rate | % | ≤0.5 | ≤1.0 | ≤2.0 | ≤3.0 | - | - | - | - | ||
8 | The number of curl | / 25mm | M1±2.5 | M1±3.0 | M1±3.5 | M1±4.0 | M1±2.5 | M1±3.0 | M1±3.5 | M1±4.0 | ||
9 | Curl rate | % | M2±2.5 | M2±3.0 | M2±3.5 | M2±4.0 | M2±2.5 | M2±3.0 | M2±3.5 | M2±4.0 | ||
10 | Resistivity | Ω.cm | ≤kX10^7 | ≤kX10^9 | ≤kX10^9 | ≤kX10^9 | ≤kX10^8 | ≤kX10^9 | ≤kX10^9 | ≤kX10^9 | ||
11 | Oil content | % | M2±0.10 | - | - | - | M3±0.10 | - | - | - | ||
12 | Coefficient of variation of breaking strength(cv) | % | ≤10.0 | - | - | - | - | - | - | - | ||